Reżistenza Liga Reżistenza Wire Spiral Tisħin Fekra Coil
FeCrAlreżistenza għolja u liga ta 'tisħin elettriku
FeCrAl reżistenza & liga tat-tisħin bil-karatteristiċi ta 'reżistenza għolja, koeffiċjent ta' temperatura baxxa ta 'reżistenza elettrika, temperatura operattiva għolja, reżistenza tajba għall-korrużjoni taħt temperatura għolja, kif ukoll il-prezz aktar baxx.
Huwa użat ħafna fil-forn elettriku industrijali, apparat elettriku tad-dar u apparat ta 'raġġi infra-aħmar bogħod.
| Prestazzjoni tan-Nomenklatura tal-Liegi | 1Cr13Al4 | 0Cr25Al5 | 0Cr21Al6 | 0Cr23Al5 | 0Cr21Al4 | 0Cr21Al6Nb | 0Cr27Al7Mo2 | |
| Kompożizzjoni kimika ewlenija (%) | Cr | 12.0-15.0 | 23.0-26.0 | 19.0-22.0 | 20.5-23.5 | 18.0-21.0 | 21.0-23.0 | 26.5-27.8 |
| Al | 4.0-6.0 | 4.5-6.5 | 5.0-7.0 | 4.2-5.3 | 3.0-4.2 | 5.0-7.0 | 6.0-7.0 | |
| Re | opportun | opportun | opportun | opportun | opportun | opportun | opportun | |
| Fe | Mistrieħ | Mistrieħ | Mistrieħ | Mistrieħ | Mistrieħ | Mistrieħ | Mistrieħ | |
| Nb0.5 | Mo1.8-2.2 | |||||||
| Max. temperatura tas-servizz kontinwu. tal-element (ºC) | 950 | 1250 | 1250 | 1250 | 1100 | 1350 | 1400 | |
| Reżistenza f'20ºC (μΩ·m) | 1.25 | 1.42 | 1.42 | 1.35 | 1.23 | 1.45 | 1.53 | |
| Densità (g/cm3) | 7.4 | 7.1 | 7.16 | 7.25 | 7.35 | 7.1 | 7.1 | |
| Konduttività termali (KJ/m·h·ºC) | 52.7 | 46.1 | 63.2 | 60.2 | 46.9 | 46.1 | 45.2 | |
| Koeffiċjent tal-linji espansjoni (α×10-6/ºC) | 15.4 | 16 | 14.7 | 15 | 13.5 | 16 | 16 | |
| Punt tat-tidwib (madwar) (ºC) | 1450 | 1500 | 150 | 1500 | 1500 | 1510 | 1520 | |
| Saħħa tat-tensjoni (N/mm2) | 580-680 | 630-780 | 630-780 | 630-780 | 600-700 | 650-800 | 680-830 | |
| Titwil fil-qsim (%) | >16 | >12 | >12 | >12 | >12 | >12 | >10 | |
| Varjazzjoni taż-żona (%) | 65-75 | 65-75 | 65-75 | 65-75 | 65-75 | 65-75 | 65-75 | |
| Frekwenza tal-liwi (F/R) | >5 | >5 | >5 | >5 | >5 | >5 | >5 | |
| Ebusija (HB) | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | |
| Ħin ta' servizz kontinwu (Sigħat/ ºC) | – | ≥80/1300 | ≥80/1300 | ≥80/1300 | ≥80/1250 | ≥50/1350 | ≥50/1350 | |
| Struttura mikrografika | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | |
| Proprjetajiet manjetiċi | Manjetiku | Manjetiku | Manjetiku | Manjetiku | Manjetiku | Manjetiku | Manjetiku | |
Wajer tond: dijametru 0.05mm-10.0mm
Wajer ċatt: ħxuna 0.2mm-1.0mm, wisa '0.08mm-40.0mm